The Influence on Fracture Resistance of Different Composite Resins and Prefabricated Posts to Restore Endodontically Treated Teeth.

Recent formulations of resin-based composites have incorporated different combinations of materials. However, the mechanical and bonding behavior of these materials with intraradicular posts are unclear. This study aimed to evaluate the effect of light-cure and dual-cure resin composite posts on the fracture resistance of endodontically-treated teeth. Materials and Methods: Ninety extracted human upper canines were selected and randomly divided into nine groups (n=10): (G1) endodontically treated teeth without endodontic posts; (G2) glass-fiber post cemented with glass-ionomer cement; (G3) endodontic post by dual-cure composite resin (Rebilda DC); (G4) endodontic post by dual-cure composite resin (Cosmecore); (G5) endodontic post by dual-cure composite resin (Bis-Core); (G6) endodontic post by light-cure composite resin; (G7) glass-fiber post customized with flowable composite resin; (G8) glass-fiber post cemented with light-cure composite resin; (G9) glass-fiber post cemented with self-adhesive resin cement. After the post insertion, all specimens were subjected to mechanical (250,000 cycles) and thermocycling (6000 cycles, 5 °C/55 °C) and immediate loading at 45 degrees in a universal testing machine until fracture. The data were analyzed by one-way ANOVA and multiple comparisons using the Fisher LSD Method (p < 0 05). Results: The mean failure loads (±SD) for the groups ranged from 100.7 ± 22.6 N to 221.9 ± 48.9 N. The G1 group (without endodontic posts) had a higher fracture strength than all experimental groups (p < 0.001). Conclusions: Within the limitations, the light- and dual-cure post technique did not present lower fracture resistance values as compared to the conventional glass-fiber post.

Effect of Curing Modes on the Mechanical Properties of Commercial Dental Resin-Based Composites: Comparison between Different LEDs and Microwave Units.

Resin-based composites (RBCs) have transformed restorative dentistry and its procedures. However, the characteristics of RBCs have been modified over the years to enhance the physical and chemical properties of the materials. This context raises the need for studies that evaluate whether the properties of the RBCs that are commercially available are clinically adequate with different curing modes. This study aimed to evaluate the mechanical behavior of commercial RBCs after undergoing different curing modes. Twenty-three RBCs of different classes were evaluated. For curing the specimens, a microwave (BMS45, Brastemp) (for 3 min at 450 W) and three LED units were used: an Emitter A Fit (Schuster (second generation)) (light-curing for 15 s with an irradiance of 1250 mW/cm2), VALO (Ultradent (third generation)) (light-curing for 15 s with an irradiance of 1100 mW/cm2), and Emitter Now Duo (Schuster (second generation)) (light-curing for 15 s with an irradiance of 1100 mW/cm2). A total of 670 RBC specimens of 8 mm in diameter and 1 mm in depth were obtained. Afterward, a biaxial flexure strength test was performed until the failure of the specimens, using a universal testing machine set at a speed of 0.5 mm/min. The same specimens were subjected to infrared spectroscopy for evaluating the degree of conversion. Tukey's test was used for multiple comparisons at a significance level of 5%. The light-curing mode did not affect the flexure strength of the RBCs (p > 0.05), but the type and shade of RBCs did so (p < 0.05). In conclusion, the type of RBC directly interferes with the mechanical behavior of the material. However, the curing modes within the same RBC did not change the mechanical properties.

Novel pulp capping material based on sodium trimetaphosphate: synthesis, characterization, and antimicrobial properties.

OBJECTIVES: To evaluate the mechanical, physicochemical, and antimicrobial properties of four different formulations containing micro- or nanoparticles of sodium trimetaphosphate (mTMP and nTMP, respectively). METHODOLOGY: Four experimental groups were used in this investigation: two mTMP groups and two nTMP groups, each containing zirconium oxide (ZrO2), and solution containing either chitosan or titanium oxide (TiO2) nanoparticles (NPs). Setting time, compression resistance, and radiopacity were estimated. The agar diffusion test was used to assess the antimicrobial activity of the formulations against five different microbial strains: Streptococcus mutans, Lactobacillus casei, Actinomyces israelii, Candida albicans, and Enterococcus faecalis. Parametric and nonparametric tests were performed after evaluating homoscedasticity data (p<0.05). RESULTS: From the properties evaluated, nTMP cements required less setting time and showed greater resistance to compression. Cements containing TiO2 showed greater radiopacity for both nTMP and mTMP. All four cement formulations showed antimicrobial activity against S. mutans and L. casei. CONCLUSION: Formulations containing nTMP have shorter setting times and higher compressive strength, and those with TiO2 nanoparticles showed antimicrobial activities. Clinical relevance: The cement containing nTMP, ZrO2, and TiO2 could be an alternative material for protecting the pulp complex.

Novel pulp capping material based on sodium trimetaphosphate: synthesis, characterization, and antimicrobial properties

Abstract Objectives: To evaluate the mechanical, physicochemical, and antimicrobial properties of four different formulations containing micro- or nanoparticles of sodium trimetaphosphate (mTMP and nTMP, respectively). Methodology: Four experimental groups were used in this investigation: two mTMP groups and two nTMP groups, each containing zirconium oxide (ZrO2), and solution containing either chitosan or titanium oxide (TiO2) nanoparticles (NPs). Setting time, compression resistance, and radiopacity were estimated. The agar diffusion test was used to assess the antimicrobial activity of the formulations against five different microbial strains: Streptococcus mutans, Lactobacillus casei, Actinomyces israelii, Candida albicans, and Enterococcus faecalis. Parametric and nonparametric tests were performed after evaluating homoscedasticity data (p<0.05). Results: From the properties evaluated, nTMP cements required less setting time and showed greater resistance to compression. Cements containing TiO2 showed greater radiopacity for both nTMP and mTMP. All four cement formulations showed antimicrobial activity against S. mutans and L. casei Conclusion: Formulations containing nTMP have shorter setting times and higher compressive strength, and those with TiO2 nanoparticles showed antimicrobial activities. Clinical relevance: The cement containing nTMP, ZrO2, and TiO2 could be an alternative material for protecting the pulp complex.

Influence of the Vehicle on the Tissue Reaction and Biomineralization of Fast Endodontic Cement

ABSTRACT Objective: To investigate the tissue response and the biomineralization ability of CER prepared with epoxy resin or water compared to Mineral Trioxide Aggregate (MTA). Material and Methods: Polyethylene tubes containing materials or empty tubes for control were inserted into the subcutaneous tissues of 30 rats. After 7, 15, 30, 60, and 90 days, the rats were killed and the tubes were removed for analysis using hematoxylin-eosin staining, von Kossa staining, and under polarized light. Inflammation was graded through a score system; the thickness of the fibrous capsule was classified as thin or thick; the biomineralization ability was recorded as present or absent. The results were statistically analyzed using the Kruskal-Wallis test (p<0.05). Results: Histologic analysis performed after 7 and 15 days for CER prepared with epoxy resin or water and for MTA showed moderate inflammation and a thick fibrous capsule (p>0.05). After 30, 60, and 90 days, mild inflammation, and a thin fibrous capsule were observed in all groups (p>0.05). Conclusion: All materials had structures positive for von Kossa and birefringent to polarized light. CER epoxy resin showed biocompatibility and biomineralization similar to CER water and MTA.

Degree of conversion of resin cements polymerized under different ceramic systems.

The aim of this study was to evaluate the degree of conversion of resin cements polymerized under different ceramic systems. Forty specimens of RelyX ARC (3M ESPE) and Maxcem Elite (Kerr) resin cements were polymerized under 5 types of dental ceramics: feldspathic, aluminum oxide-reinforced, aluminum oxide-based strengthened with zirconium oxide, leucite-reinforced, and lithium disilicate-reinforced. Measurements of the degree of conversion of the resin cements were performed 10 minutes, 1 hour, and 24 hours after curing using a Fourier transform infrared spectrophotometer. The values were subjected to a 3-way repeated-measures analysis of variance, and the means were compared with the Fisher protected least significant difference test (α = 0.05). The study findings showed that RelyX ARC resin cement displayed a higher degree of conversion than Maxcem Elite (P < 0.05). The degree of conversion was significantly lower for RelyX ARC polymerized under aluminum oxide ceramic and aluminum oxide ceramic strengthened with zirconium oxide (P < 0.05). For Maxcem Elite, there was no significant difference in the degree of conversion attained under the various ceramics (P > 0.05). For both cements, the degree of conversion increased gradually up to 24 hours after curing (P < 0.05). The ceramic system used directly influenced the degree of conversion of RelyX ARC. Both resin cements displayed an increase in the degree of conversion over time.

Resin-modified glass ionomer containing calcium glycerophosphate: physico-mechanical properties and enamel demineralization.

BACKGROUND: Sources of calcium and phosphate have been added to dental restorative materials to improve their anticaries effect. OBJECTIVE: This study evaluated the effect of adding calcium glycerophosphate (CaGP) to resin-modified glass ionomer cement (RMGIC) on the physico-mechanical properties, ion release, and enamel demineralization. Material and Methods: Specimens were fabricated for each experimental group: RMGIC without CaGP (Control), RMGIC with 1, 3 and 9% CaGP. To determine the release of fluoride (F), calcium (Ca) and phosphorus (P), six specimens were immersed in demineralization and remineralization solutions for 15 days. In another experimental trial, the following physico-mechanical properties were evaluated at time intervals of 1 and 7 days after fabrication: compressive strength (n=12), diametral tensile strength (n=12), surface hardness of material (n=6) and the degree of conversion of monomers (n=8). To study enamel demineralization, specimens (n=12) were attached to enamel blocks and submitted to pH-cycling. Subsequently, surface and cross-sectional hardness and the concentration of F, Ca and P in enamel were determined. RESULTS: The addition of CaGP to RMGIC led to higher mean release of F, Ca and P when compared with control (p<0.001). Mechanical properties were within the range of those of the ionomer cements after addition of 1% and 3% CaGP. The degree of conversion did not differ between groups at the 1st and the 7th day (p>0.439). The addition of 3% and 9% CaGP reduced mineral loss and increased F, Ca and P in the enamel when compared with control (p<0.05). CONCLUSION: The addition of 3% CaGP in RMGIC increased the release of F, P and Ca, reduced enamel demineralization, and maintained the physico-mechanical properties within the parameters for this material.

Ion release, antimicrobial and physio-mechanical properties of glass ionomer cement containing micro or nanosized hexametaphosphate, and their effect on enamel demineralization.

OBJECTIVES: To evaluate the effects of hexametaphosphate microparticles (mHMP) or nanoparticles (nHMP) incorporated in glass ionomer cement (GIC) on antimicrobial and physico-mechanical properties, fluoride (F) release, and enamel demineralization. MATERIAL AND METHODS: HMP solutions were obtained at concentrations of 1, 3, 6, 9, and 12%, for screening of antimicrobial activity. Next, mHMP or nHMP at 6, 9, and 12% were incorporated into a resin-modified GIC and the antibacterial activity was evaluated. The resistance to diametral tensile and compressive strength, surface hardness, and degree of monomer conversion as well as F and HMP releases of GICs were determined. Furthermore, specimens were attached to enamel blocks and submitted to pH-cycling, and mineral loss was determined. Parametric and non-parametric tests were performed, after checking data homoscedasticity (p < 0.05). RESULTS: HMP solutions at 6, 9, and 12% demonstrated the best antibacterial activity. GIC containing HMP showed better antibacterial effects at 9 and 12% for nHMP. Regarding F and HMP releases, the highest levels of release occurred for groups containing 9 and 12% nHMP. With the increase in HMP concentration, there was lower mineral loss. However, the incorporation of mHMP or nHMP in GIC reduced values of physico-mechanical properties when compared to the control GIC. CONCLUSIONS: nHMP improves antimicrobial activity and fluoride release, and decreases enamel demineralization, but reduces the physico-mechanical properties of GIC. CLINICAL RELEVANCE: The association of GIC/HMP could be an alternative material for patients at high risk for dental caries and could be indicated for low-stress regions or provisional restorations.

Degree of conversion of resin cements polymerized under different thicknesses of feldspathic porcelain

Aim The aim of this study is to evaluate the degree of conversion (DC) of resin cements polymerized under different thicknesses of feldspathic dental ceramic. Methods: Forty samples of RelyX ARC and RelyX Veneer resin cements were polymerized under Starlight feldspathic ceramic discs (DeguDent Gmbh) with 0.5 mm, 1.2 mm, 1.8 mm, and 2.4 mm in thickness. The control group was cured without the interposition of ceramic. The DC measurements were performed 10 minutes, 1 hour, and 24 hours after the light-activation in a Nexus 670 FTIR spectrophotometer. Data were analyzed by two-way repeated measure ANOVA and Fisher PLSD test. Results: The RelyX ARC showed higher DC for all ceramic thicknesses. There was significant decrease in DC related to an increase in ceramic thickness. For RelyX ARC, the values of DC obtained after 1 hour and 24 hours did not differ statistically between them, but they were higher than those analyzed after 10 minutes. For RelyX Veneer cement, there was gradual increase in the DC up to 24 hours. Conclusion: The higher the thicknesses of ceramic, the lower DC of the resin cement

Resin-modified glass ionomer containing calcium glycerophosphate: physico-mechanical properties and enamel demineralization

Abstract Sources of calcium and phosphate have been added to dental restorative materials to improve their anticaries effect. Objective This study evaluated the effect of adding calcium glycerophosphate (CaGP) to resin-modified glass ionomer cement (RMGIC) on the physico-mechanical properties, ion release, and enamel demineralization. Material and Methods: Specimens were fabricated for each experimental group: RMGIC without CaGP (Control), RMGIC with 1, 3 and 9% CaGP. To determine the release of fluoride (F), calcium (Ca) and phosphorus (P), six specimens were immersed in demineralization and remineralization solutions for 15 days. In another experimental trial, the following physico-mechanical properties were evaluated at time intervals of 1 and 7 days after fabrication: compressive strength (n=12), diametral tensile strength (n=12), surface hardness of material (n=6) and the degree of conversion of monomers (n=8). To study enamel demineralization, specimens (n=12) were attached to enamel blocks and submitted to pH-cycling. Subsequently, surface and cross-sectional hardness and the concentration of F, Ca and P in enamel were determined. Results The addition of CaGP to RMGIC led to higher mean release of F, Ca and P when compared with control (p<0.001). Mechanical properties were within the range of those of the ionomer cements after addition of 1% and 3% CaGP. The degree of conversion did not differ between groups at the 1st and the 7th day (p>0.439). The addition of 3% and 9% CaGP reduced mineral loss and increased F, Ca and P in the enamel when compared with control (p<0.05). Conclusion The addition of 3% CaGP in RMGIC increased the release of F, P and Ca, reduced enamel demineralization, and maintained the physico-mechanical properties within the parameters for this material.

Dentinal tubule obliteration using toothpastes containing sodium trimetaphosphate microparticles or nanoparticles.

OBJECTIVES: This in vitro study evaluated the effect of microparticles (TMPmicro) or nanoparticles (TMPnano) TMP associated with fluoride (F) in toothpaste formulations on the obliteration of dentinal tubules (DT). MATERIALS AND METHODS: The dentinal tubules of bovine dentin blocks were unobstructed by immersion in 37% phosphoric acid solution. Blocks (n = 20/group) underwent mechanical brushing (2×/day) during 7 days with toothpastes: placebo, 1100 ppm F, and 1100 with 3% TMPmicro or 3% TMPnano. After that, ten blocks of each group were immersed in citric acid (pH 3.2) for 1 min. The number, diameter and area of unobstructed DT, atomic % of chemical elements from precipitates, and the mineral concentration were quantified. Data were submitted to two-way ANOVA, followed by Student-Newman-Keuls test (P < 0.05). RESULTS: Toothpastes containing TMPmicro and TMPnano promoted greater obliteration of DT and greater mineral concentration compared to other groups (P < 0.05). Placebo and 1100 ppm F group presented similar obliteration but 1100 ppm F group promoted higher mineral concentration. Higher Ca/P ratios were observed in groups treated with TMP; the acid challenge reduced Ca/P ratio for all groups. The atomic % of C and N was significantly lower for TMP toothpastes before acid challenge, but increased afterwards. CONCLUSIONS: It was concluded that the addition of TMPmicro or TMPnano to F toothpastes produced greater obliteration of dentinal tubules and higher mineral concentration when compared with 1100 ppm F. CLINICAL RELEVANCE: By the addition of TMP, fluoride toothpastes may occlude the dentinal tubules, with potential to reduce dentin hypersensitivity.

Cytotoxic effects of new MTA-based cement formulations on fibroblast-like MDPL-20 cells.

The present study aimed at evaluating the cytotoxic effects of a novel cement called CER on periodontal fibroblast-like cells of mice (MDPL-20), in comparison with different formulations of Mineral Trioxide Aggregate (MTA), by means of the cell viability test (MTT) and cell morphology analysis. Thirty-two round-shaped samples were fabricated with the following cements: white MTA, white and gray CER and experimental white MTA. The samples were immersed in serum-free culture medium for 24 hours or 7 days (n = 16). The extracts (culture medium + components released from the cements) were applied for 24 hours to previously cultured cells (40.000 cells/cm2) in the wells of 24-well plates. Cells seeded in complete culture medium were used as a negative control. Cell viability was assessed using the MTT assay. Two samples of each cement were used for cell morphology analysis by Scanning Electron Microscopy (SEM). The extracts obtained at the 7-day period presented higher cytotoxicity compared with the 24-hour period (p < 0.05). The gray CER obtained at 24 hours presented the highest cytotoxic effect, whereas the experimental white MTA presented the lowest, similar to the control (p > 0.05). However, at the 7-day period, the experimental white MTA presented no significant difference in comparison with the other cements (p > 0.05). At the 7-day period, CER cement presented cytotoxic effects on fibroblast-like cells, similar to different MTA formulations. However, the immersion period in the culture medium influenced the cytotoxicity of the cements, which was greater for CER cement at 24 hours.

Cytotoxic effects of new MTA-based cement formulations on fibroblast-like MDPL-20 cells

Abstract The present study aimed at evaluating the cytotoxic effects of a novel cement called CER on periodontal fibroblast-like cells of mice (MDPL-20), in comparison with different formulations of Mineral Trioxide Aggregate (MTA), by means of the cell viability test (MTT) and cell morphology analysis. Thirty-two round-shaped samples were fabricated with the following cements: white MTA, white and gray CER and experimental white MTA. The samples were immersed in serum-free culture medium for 24 hours or 7 days (n = 16). The extracts (culture medium + components released from the cements) were applied for 24 hours to previously cultured cells (40.000 cells/cm2) in the wells of 24-well plates. Cells seeded in complete culture medium were used as a negative control. Cell viability was assessed using the MTT assay. Two samples of each cement were used for cell morphology analysis by Scanning Electron Microscopy (SEM). The extracts obtained at the 7-day period presented higher cytotoxicity compared with the 24-hour period (p < 0.05). The gray CER obtained at 24 hours presented the highest cytotoxic effect, whereas the experimental white MTA presented the lowest, similar to the control (p > 0.05). However, at the 7-day period, the experimental white MTA presented no significant difference in comparison with the other cements (p > 0.05). At the 7-day period, CER cement presented cytotoxic effects on fibroblast-like cells, similar to different MTA formulations. However, the immersion period in the culture medium influenced the cytotoxicity of the cements, which was greater for CER cement at 24 hours.

Effect of Trimetaphosphate and Fluoride Association on Hydroxyapatite Dissolution and Precipitation In Vitro

The present study analyzed the action of sodium trimetaphosphate (TMP) and/or fluoride on hydroxyapatite. Hydroxyapatite powder was suspended in different solutions: deionized water, 500 µg F/mL, 1,100 µg F/mL, 1%TMP, 3%TMP, 500 µg F/mL plus 1%TMP and 500 µg F/mL plus 3%TMP. The pH value of the solutions was reduced to 4.0 and after 30 min, raised to 7.0 (three times). After pH-cycling, the samples were analyzed by X-ray diffraction and infrared spectroscopy. The concentrations of calcium fluoride, fluoride, calcium and phosphorus were also determined. Adding 1% or 3% TMP to the solution containing 500 µg F/mL produced a higher quantity of calcium fluoride compared to samples prepared in a 1,100 µg F/mL solution. Regarding the calcium concentration, samples prepared in solutions of 1,100 µg F/mL and 500 µg F/mL plus TMP were statistically similar and showed higher values. Using solutions of 1,100 µg F/mL and 500 µg F/mL plus TMP resulted in a calcium/phosphorus ratio close to that of hydroxyapatite. It is concluded that the association of TMP and fluoride favored the precipitation of a more stable hydroxyapatite.

O presente estudo avaliou a ação do trimetafosfato de sódio (TMP) e/ou fluoreto sobre a hidroxiapatita. Pó de hidroxiapatita foi suspenso em diferentes soluções: água deionizada, 500 µg F/mL, 1100 µg F/mL, 1%TMP, 3%TMP, 500 µg F/mL adicionado a 1%TMP e 500 µg F/mL associado a 3%TMP. O pH das soluções foi reduzido para 4,0 e depois de 30 min, elevado para 7,0 (três vezes). Depois do processo de ciclagem de pH, as amostras foram analisadas por difração de raios-X e espectroscopia por infravermelho. As concentrações de fluoreto de cálcio, fluoreto, cálcio e fósforo também foram determinadas. A adição de 1% ou 3% TMP na solução contendo 500 µg F/mL produziu uma maior quantidade de fluoreto de cálcio comparado às amostras tratadas com uma solução de 1100 µg F/mL. A respeito da concentração de cálcio, amostras tratadas com soluções de 1100 µg F/mL e 500 µg F/mL adicionado ao TMP foram estatisticamente similares e mostraram maiores valores. Soluções de 1100 µg F/mL e 500 µg F/mL adicionado ao TMP resultaram em uma proporção molar Ca/P mais próxima à da hidroxiapatita. Conclui-se que a associação de TMP e F favoreceu a precipitação de uma hidroxiapatita mais estável.

Influência da fotopolimerização e termociclagem na adesão de compósitos ortodônticos / Influence of photopolymerization and thermocycling on the adhesion of orthodontic composites

Neste trabalho avaliou-se a influência de choques térmicos e fatores relacionados à fotopolimerização na adesão de acessórios ortodônticos ao dente. Para tanto, foram utilizados três compósitos adesivos comerciais. Foram utilizadas duas fontes de luz LED para polimerização dos compósitos com diferentes tempos de exposição à irradiação. As amostras foram divididas em dois grupos, sendo um deles sujeito à termociclagem. A adesão dos compósitos foi avaliada através da resistência ao cisalhamento. Entre os compósitos estudados, Fill Magic e Transbond mostraram o mais baixo e a mais alta resistência ao cisalhamento, respectivamente. A fonte de luz com maior densidade de potência promoveu a maior resistência ao cisalhamento. A resistência ao cisalhamento dos compósitos Fill Magic e Ortho Lite foi influenciada pela termociclagem.

This study evaluated the influence of thermal shock, and factors related to photopolymerization on the adhesion of orthodontic accessories to teeth. Three light-cured composite adhesives were used. Two LED light sources were used to cure the adhesive composites at different times of the light irradiation. The samples were divided into two groups, with one group subjected to thermocycling. The adhesion of the composites was evaluated through shear bond strength. Fill Magic and Transbond showed the lowest and highest shear bond strength, respectively. The light-curing unit with higher power density promoted greater shear bond strength. The shear bond strength of the Fill Magic and Ortho Lite adhesives was influenced by thermocycling.

Effect of trimetaphosphate and fluoride association on hydroxyapatite dissolution and precipitation in vitro.

The present study analyzed the action of sodium trimetaphosphate (TMP) and/or fluoride on hydroxyapatite. Hydroxyapatite powder was suspended in different solutions: deionized water, 500 µg F/mL, 1,100 µg F/mL, 1%TMP, 3%TMP, 500 µg F/mL plus 1%TMP and 500 µg F/mL plus 3%TMP. The pH value of the solutions was reduced to 4.0 and after 30 min, raised to 7.0 (three times). After pH-cycling, the samples were analyzed by X-ray diffraction and infrared spectroscopy. The concentrations of calcium fluoride, fluoride, calcium and phosphorus were also determined. Adding 1% or 3% TMP to the solution containing 500 µg F/mL produced a higher quantity of calcium fluoride compared to samples prepared in a 1,100 µg F/mL solution. Regarding the calcium concentration, samples prepared in solutions of 1,100 µg F/mL and 500 µg F/mL plus TMP were statistically similar and showed higher values. Using solutions of 1,100 µg F/mL and 500 µg F/mL plus TMP resulted in a calcium/phosphorus ratio close to that of hydroxyapatite. It is concluded that the association of TMP and fluoride favored the precipitation of a more stable hydroxyapatite.

Effect of sodium trimetaphosphate on hydroxyapatite solubility: an in vitro study.

This study evaluated the effect of different concentrations of sodium trimetaphosphate (TMP) with and without fluoride (F) on the concentration of calcium (Ca), phosphorus (P) and F in hydroxyapatite (HA). Synthetic HA powder (0.15 g) was suspended (n=6) in solutions (75 mL) of TMP at 0%, 0.1%, 0.2%, 0.4%, 0.6%, 0.8%, 1.0%, 2.0%, 4.0%, 6.0%, 8.0% and 10% concentrations in the presence and absence of 100 ppm F and subjected to a pH-cycling process. The precipitates were filtrated, dried at 70° C for 24 h and ground onto a fine powder. The concentrations of F (KOH (CaF2) and HCl (FA) soluble), Ca (Arsenazo III), and P (molybdate method) in HA were determined. The Ca P, and Ca/P ratio data were subjected to Tukey's test and the F data were subjected to Student-Newman-Keuls test (p<0.05). The addition of TMP to the samples reduced F deposition to 98% (p<0.001). The groups containing 100 ppm F and 0.4% or 0.6% TMP exhibited a higher Ca concentration than the group containing only 100 ppm F (p<0.05). Furthermore, the HA treated with 0.2% and 0.4% TMP and 100 ppm F showed a higher Ca/P ratio than the other groups (p<0.001). In conclusion, TMP at 0.2%, 0.4% and 0.6% concentrations combined with F seemed to be able to precipitate HA with low solubility. However, especially at high concentrations, TMP interferes with F deposition on HA.

Effect of Sodium Trimetaphosphate on Hydroxyapatite Solubility: An In Vitro Study

This study evaluated the effect of different concentrations of sodium trimetaphosphate (TMP) with and without fluoride (F) on the concentration of calcium (Ca), phosphorus (P) and F in hydroxyapatite (HA). Synthetic HA powder (0.15 g) was suspended (n=6) in solutions (75 mL) of TMP at 0%, 0.1%, 0.2%, 0.4%, 0.6%, 0.8%, 1.0%, 2.0%, 4.0%, 6.0%, 8.0% and 10% concentrations in the presence and absence of 100 ppm F and subjected to a pH-cycling process. The precipitates were filtrated, dried at 70° C for 24 h and ground onto a fine powder. The concentrations of F (KOH (CaF2) and HCl (FA) soluble), Ca (Arsenazo III), and P (molybdate method) in HA were determined. The Ca P, and Ca/P ratio data were subjected to Tukey's test and the F data were subjected to Student-Newman-Keuls test (p<0.05). The addition of TMP to the samples reduced F deposition to 98% (p<0.001). The groups containing 100 ppm F and 0.4% or 0.6% TMP exhibited a higher Ca concentration than the group containing only 100 ppm F (p<0.05). Furthermore, the HA treated with 0.2% and 0.4% TMP and 100 ppm F showed a higher Ca/P ratio than the other groups (p<0.001). In conclusion, TMP at 0.2%, 0.4% and 0.6% concentrations combined with F seemed to be able to precipitate HA with low solubility. However, especially at high concentrations, TMP interferes with F deposition on HA.

Este estudo avaliou o efeito de diferentes concentrações de trimetafosfato de sódio (TMP) com e sem fluoreto (F) nas concentrações de cálcio (Ca), fósforo (P) e F na hidroxiapatita (HA). Pó de HA sintético (0,15 g) foi suspenso (n=6) em soluções (75 mL) de TMP com concentrações de 0%, 0,1%, 0,2%, 0,4%, 0,6%, 0,8%, 1,0%, 2,0%, 4,0%, 6,0%, 8,0% e 10% na presença ou na ausência de 100 ppm F e foram submetidas ao processo de ciclagem de pH. O precipitado foi filtrado seco a 70°C por 24 h e triturado em um pó fino. As concentrações de F (solúvel em KOH: CaF2, e em HCl: FA), Ca (Arsenazo III) e P (método do molibdato) foram determinadas na HA. Os dados de Ca, P e de proporção Ca/P foram submetidos ao teste de Tukey e os dados de F ao teste Student-Newman-Keuls (p<0,05). A adição de TMP reduziu a deposição de F em 98% (p<0,001). Os grupos contendo 100 ppm F e TMP 0,4% e 0,6% apresentaram maiores concentrações de Ca do que o grupo contendo somente 100 ppm F (p<0,05). Além disso, a HA tratada com 0,2% e 0,4% de TMP e 100 ppm F apresentou maiores proporções Ca/P em relação aos demais grupos (p<0,001). Em conclusão, TMP nas concentrações de 0,2%, 0,4% e 0,6% quando associado ao F é capaz de precipitar uma HA com menor solubilidade. Entretanto, especialmente em altas concentrações, TMP interfere com a deposição de F na HA.

Effect of light curing modes on mechanical properties of direct and indirect composites.

OBJECTIVE: To evaluate the degree of conversion (DC), flexural strength (FS) and Knoop microhardness (KHN) of direct and indirect composite resins polymerized with different curing systems. MATERIALS AND METHODS: Specimens of direct (Z250, 3M/Espe) and indirect (Sinfony, 3M/Espe) restorative materials were made and polymerized using two light curing units: XL2500 (3M/Espe) and Visio system (3M/Espe). Absorption spectra of both composites were obtained on a FTIR spectrometer in order to calculate the DC. FS was evaluated in a universal testing machine and surface microhardness was performed in a microhardness tester (50gf/15s). DC, FS and KHN data were submitted to two-way ANOVA and Tukey's test (α = 0.05). RESULTS: Z250 showed higher DC, FS and KHN compared with Sinfony when the polymerization was carried out with XL2500 (p < 0.05). However, there is no statistical difference in DC between the materials when Visio was used (p > 0.05). Visio showed higher DC and KHN for Z250 and Sinfony than the values obtained using XL2500 light curing (p < 0.05). For FS, no significant difference between curing units was found (p > 0.05). CONCLUSION: Even though the Visio system could increase DC and KHN for some direct and indirect composites, compared with the conventional halogen curing unit, a high number of monomers did not undergo conversion during the polymerization.

Influence of heat treatment and oxygen doping on the mechanical properties and biocompatibility of titanium-niobium binary alloys.

The most commonly used titanium (Ti)-based alloy for biological applications is Ti-6Al-4V, but some studies associate the vanadium (V) with the cytotoxic effects and adverse reactions in tissues, while aluminum (Al) has been associated with neurological disorders. Ti-Nb alloys belong to a new class of Ti-based alloys with no presence of Al and V and with elasticity modulus values that are very attractive for use as a biomaterial. It is well known that the presence of interstitial elements (such as oxygen, for example) changes the mechanical properties of alloys significantly, particularly the elastic properties, the same way that heat treatments can change the microstructure of these alloys. This article presents the effect of heat treatment and oxygen doping in some mechanical properties and the biocompatibility of three alloys of the Ti-Nb system, characterized by density measurements, X-ray diffraction, optical microscopy, Vickers microhardness, in vitro cytotoxicity, and mechanical spectroscopy.